纤度 Linear Density | 孔数 Filaments | 断裂强力 Strength at Break | 断裂强度 Tenacity | 断裂伸长率 Elongation at Break | 干热收缩率 (190℃,15min 0.01cN/dtex) Hot Air Shrinkage | ||
Denier | Dtex | F | N | cN/dtex | g/d | % | % |
220 | 245 | 48 | 16.17 | ≥6.50 | ≥7.35 | 22 | 2.8 |
250 | 280 | 48 | 18.76 | ≥6.70 | ≥7.57 | 22 | 2.8 |
420 | 470 | 96 | 31.96 | ≥6.80 | ≥7.68 | 24 | 2.3 |
500 | 555 | 96 | 39.1 | ≥6.90 | ≥7.80 | 24 | 2.3 |
840 | 930 | 192 | 65.10 | ≥7.00 | ≥7.91 | 24 | 2 |
1000 | 1110 | 192 | 77.7 | ≥7.00 | ≥7.91 | 24 | 2 |
1300 | 1440 | 192 | 103.68 | ≥7.20 | ≥8.14 | 24 | 2 |
1500 | 1670 | 192 | 120.24 | ≥7.20 | ≥8.14 | 24 | 2.3 |
2000 | 2220 | 384 | 159.84 | ≥7.20 | ≥8.14 | 24 | 2.3 |
3000 | 3330 | 384 | 239.76 | ≥7.20 | ≥8.14 | 24 | 2.3 |