纤度 Linear Density | 孔数 Filaments | 断裂强力 Strength at Break | 断裂强度 Tenacity | 断裂伸长率 Elongation at Break | 干热收缩率 (177℃,10min 0.05cN/dtex) Hot Air Shrinkage | ||
Denier | Dtex | F | N | cN/dtex | g/d | % | % |
1000 | 1110 | 192 | 91.02 | ≥8.20 | ≥9.27 | 11.2 | 12.5 |
1500 | 1666 | 192 | 139.94 | ≥8.40 | ≥9.49 | 11.6 | 12.5 |
2000 | 2220 | 260/384 | 184.6 | ≥8.30 | ≥9.38 | 12 | 12.5 |
3000 | 3330 | 384 | 276.39 | ≥8.30 | ≥9.38 | 12 | 13 |
4600 | 4440 | 576/768 | 368.52 | ≥8.30 | ≥9.38 | 12 | 13 |
5000 | 5550 | 768 | 455.1 | ≥8.20 | ≥9.27 | 12 | 13 |
6000 | 6660 | 768 | 539.46 | ≥8.10 | ≥9.25 | 12 | 13 |
8000 | 9100 | 1040 | 728 | ≥8.00 | ≥9.04 | 12.5 | 13 |