纤度 Linear Density | 孔数 Filaments | 断裂强力 Strength at Break | 断裂强度 Tenacity | 断裂伸长率 Elongation at Break | 干热收缩率 (177℃,10min 0.05cN/dtex) Hot Air Shrinkage | ||
Denier | Dtex | F | N | cN/dtex | g/d | % | % |
250 | 280 | 48 | 21.84 | ≥7.80 | ≥8.81 | 13 | 7.5 |
300 | 335 | 48 | 26.13 | ≥7.80 | ≥8.81 | 13 | 7.5 |
420 | 470 | 96 | 37.6 | ≥8.00 | ≥9.04 | 13.5 | 6.5 |
500 | 560 | 96 | 44.8 | ≥8.00 | ≥9.04 | 13.5 | 6.5 |
840 | 940 | 192 | 76.14 | ≥8.10 | ≥9.15 | 13.5 | 6.5 |
1000 | 1125 | 192 | 92.25 | ≥8.20 | ≥9.27 | 14 | 6.5 |
1500 | 1690 | 192 | 141.96 | ≥8.40 | ≥9.49 | 15 | 6.5 |
2000 | 2240 | 260/384 | 185.92 | ≥8.30 | ≥9.38 | 15 | 6.5 |
2600 | 2880 | 384 | 239.04 | ≥8.30 | ≥9.38 | 15 | 6.5 |
3000 | 3400 | 384 | 282.2 | ≥8.30 | ≥9.38 | 15 | 6.5 |
4000 | 4533 | 576/768 | 376.24 | ≥8.30 | ≥9.38 | 16 | 6.5 |
5000 | 5610 | 768 | 460.02 | ≥8.20 | ≥9.27 | 16 | 6.5 |
6000 | 6720 | 768 | 544.32 | ≥8.10 | ≥9.15 | 16 | 6 |
8000 | 9088 | 1040 | 727.04 | ≥8.00 | ≥9.04 | 18 | 5 |