纤度 Linear Density | 孔数 Filaments | 断裂强力 Strength at Break | 断裂强度 Tenacity | 断裂伸长率 Elongation at Break | 干热收缩率 (190℃,15min 0.01cN/dtex) Hot Air Shrinkage | ||
Denier | Dtex | F | N | cN/dtex | g/d | % | % |
220 | 245 | 48 | 16.17 | ≥6.60 | ≥7.46 | 21 | 3.5 |
250 | 280 | 48 | 19.04 | ≥6.80 | ≥7.68 | 21 | 3.5 |
300 | 335 | 48 | 23.7 | ≥6.80 | ≥7.68 | 21 | 3.5 |
420 | 470 | 96 | 32.9 | ≥7.00 | ≥7.91 | 21 | 3 |
500 | 555 | 96 | 39.41 | ≥7.10 | ≥8.02 | 21 | 3 |
1000 | 1110 | 192 | 78.81 | ≥7.10 | ≥8.02 | 21 | 3 |
1500 | 1670 | 192 | 121.91 | ≥7.30 | ≥8.25 | 24 | 3 |
2000 | 2220 | 384 | 162.06 | ≥7.30 | ≥8.25 | 24 | 3.5 |
3000 | 3330 | 384 | 243.09 | ≥7.30 | ≥8.25 | 24 | 3.5 |